DESCRIPTION
C37000, Engraving brass, are 60/40 alpha-beta brasses with lead added to give free machining properties. They should not be used for acid etched work, for which the single phase alpha brasses should be used.
CHEMICAL COMPOSITION
| Elements | Min(%) | Max(%) |
| Cu | 59.00 | 62.00 |
| Pb | 0.8 | 1.50 |
| Fe | - | 0.15 |
| Total Others | - | 0.40 |
| Zn | Remainder |
MECHANICAL PROPERTIES ACCORDING TO ASTM B124
Mechanical Property requirement, if any, are to be established by agreement between the manufacturer and the purchaser.
| PHYSICAL PROPERTIES |
| Melting Point -Liquidus°F | 1650 |
| Melting Point -Solidus°F | 1630 |
| Density lb/cu in.at 68°F | 0.304 |
| Specific Gravity | 8.41 |
| Electrical Conductivity %IACS at 68°F | 27 |
| Thermal Conductivity Btu/ sq ft/ft hr/°F at 68°F | 69 |
| Coefficient of Thermal Expansion 68-57210-6 per°F(68-572° | 11.6 |
| Specific Heat Capacity Btu/lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tension ksi | 15000 |
| Modulus of Rigidity ksi | 5600 |
| FABRICATION PROPERTIES |
| Technique | Suitability |
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas shielded Are Welding | Not Recommended |
| Coated Metal Are Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Fair |
| Capacity for Being Hot Formed | Excellent |
| Machinability Rating | 70 |