36000 (HO2) Free machining brass, produced from a combination of copper and zinc, has the highest machinability of all copper alloys, and is the standard against which all the others are compared to. 360 Brass, known for its strength and resistance to corrosion with properties closely resembling that of steel, is one of the most popular copper alloys used today. 360 Brass can be precision machined easily. Although ductile in its softened state, 360 Brass is a strong material to work with and maintains its strength even under some of the most demanding conditions. 360 Brass forms a thin protective“patina”, which, unlike steel and iron, will not rust when exposed to the atmosphere. As a high-density material, 360 Brass is ideal for heavy industrial parts. 360 Brass is also valued for its high polished finish. 360 Brass is available in rounds, flats, squares, hexagons, tube, plate, and sheet.
CHEMICAL COMPOSITION
| Elements | Min(%) | Max(%) |
| Cu | 60.00 | 63.00 |
| Pb | 2.50 | 3.00 |
| Fe | - | 0.35 |
| Total Others | - | 0.50 |
| Zn | Remainder |
MECHANICAL PROPERTIES ACCORDING TO UNSJ463 (AS PER TEMPER HO2)
| Range (Inch) | From | To | UTS Min (Ksi) | PS Min (Ksi) | Elongation Min(%) | Hardness Min(HRB) | Hardness Max(HRB) |
| Round(Dia) | 0.059 | 0.500 | 57 | 25 | 7 |
|
|
| 0.500 | 1.000 | 55 | 25 | 10 | 60 | 80 |
| 1.000 | 2.000 | 50 | 20 | 15 | 55 | 75 |
| 2.000 | 2.953 | 45 | 15 | 20 | 45 | 70 |
| Hex(A/F) | 0.118 | 0.500 | 57 | 25 | 7 |
|
|
| 0.500 | 1.000 | 55 | 25 | 10 | 55 | 80 |
| 1.000 | 2.000 | 50 | 20 | 15 | 45 | 80 |
| 2.000 | 2.756 | 45 | 15 | 20 | 40 | 65 |
| Square (A/F | 0.118 | 0.500 | 57 | 25 | 7 |
|
|
| 0.500 | 1.000 | 55 | 25 | 10 | 55 | 80 |
| 1.000 | 2.000 | 50 | 20 | 15 | 45 | 80 |
| 2.000 | 2.362 | 45 | 15 | 20 | 40 | 65 |
| Octagon (A/F) | 0.118 | 0.500 | 57 | 25 | 7 |
|
|
| 0.500 | 1.000 | 55 | 25 | 10 | 55 | 80 |
| 1.000 | 2.000 | 50 | 20 | 15 | 45 | 80 |
| 2.000 | 2.362 | 45 | 15 | 20 | 40 | 65 |
| Rectangle | Thickness | 0.118 | 0.500 | 50 | 25 | 10 | 45 | 85 |
| Width | 0.118 | 1.000 |
| Thickness | 0.118 | 0.500 | 45 | 17 | 15 | 35 | 70 |
| Width | 1.000 | 2.756 |
| Thickness | 0.500 | 1.969 | 45 | 17 | 15 | 40 | 80 |
| Width | 0.079 | 2.000 |
| Thickness | 0.500 | 1.968 | 40 | 15 | 20 | 35 | 70 |
| Width | 2.000 | 2.756 |
| Range(mm) | From | To | UTS Min(MPa) | PS Min(MPa) | Elongation Min (%) | Hardness Min(HRB) | Hardness Max(HRB) |
| Round(Dia) | 1.5 | 12 | 395 | 170 | 7 |
|
|
| 12 | 25 | 380 | 170 | 10 | 60 | 80 |
| 25 | 50 | 345 | 140 | 15 | 55 | 75 |
| 50 | 75 | 310 | 105 | 20 | 45 | 70 |
| Hex(A/F) | 3 | 12 | 395 | 170 | 7 |
|
|
| 12 | 25 | 380 | 170 | 10 | 55 | 80 |
| 25 | 50 | 345 | 140 | 140 | 45 | 80 |
| 50 | 70 | 310 | 105 | 20 | 40 | 65 |
| Square (A/F) | 3 | 12 | 395 | 170 | 7 |
|
|
| 12 | 25 | 380 | 170 | 10 | 55 | 80 |
| 25 | 50 | 345 | 140 | 15 | 45 | 80 |
| 50 | 60 | 310 | 105 | 20 | 40 | 65 |
| Octagon(A/F) | 3 | 12 | 395 | 170 | 7 |
|
|
| 12 | 25 | 380 | 170 | 10 | 55 | 80 |
| 25 | 50 | 345 | 140 | 15 | 45 | 80 |
| 50 | 60 | 310 | 105 | 20 | 40 | 65 |
| Rectangle | Thickness | 3 | 12 | 345 | 170 | 10 | 45 | 85 |
| Width | 4 | 25 |
| Thickness | 3 | 12 | 310 | 115 | 15 | 35 | 70 |
| Width | 25 | 70 |
| Thickness | 12 | 50 | 310 | 115 | 15 | 40 | 80 |
| Width | 4 | 50 |
| Thickness | 12 | 50 | 275 | 105 | 20 | 35 | 70 |
| Width | 50 | 70 |
| PHYSICAL PROPERTIES |
| Melting Point -Liquidus°F | 1650 |
| Melting Point -Solidus°F | 1630 |
| Density lb/cu in.at 68°F | 0.307 |
| Specific Gravity | 8.5 |
| Electrical Conductivity %IACS at 68°F | 26 |
| Thermal Conductivity Btu/ sq ft/ft hr/°F at 68°F | 67 |
| Coefficient of Thermal Expansion 68-57210-6 per°F(68-572° | 11.4 |
| Specific Heat Capacity Btu/lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tension ksi | 14000 |
| Modulus of Rigidity ksi | 5300 |
| FABRICATION PROPERTIES |
| Melting Point -Liquidus°F | 1650 |
| Melting Point -Solidus°F | 1630 |
| Densitylb/cu in.at 68°F | 0.307 |
| Specific Gravity | 8.5 |
| Electrical Conductivity% IACS at 68°F | 26 |
| Thermal ConductivityBtu/ sq ft/ft hr/°F at 68°F | 67 |
| Coefficient of Thermal Expansion 68-57210-6 per°F(68-57. | 11.4 |
| Specific Heat CapacityBtu/lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 14000 |
| Modulus of Rigidityksi | 5300 |
| Machinability Rating | 100 |