UNS C27200 yellow brass has a copper content of not less than 62%,CuZn37 is the major brass alloy for the cold forming process Even though brasses with lower Zinc content have better cold forming properties, CuZn37 is the most used alloy. Reasons for this are on the one hand economical due to lower price of Zinc compared to copper on the other hand the forming properties of this alloy meet the demand of many applications.
CHEMICAL COMPOSITION
| Elements | Min(%) | Max(%) |
| Cu | 62.00 | 65.00 |
| Pb | - | 0.07 |
| Fe | - | 0.07 |
| Total Others | - | 0.30 |
| Zn | Remainder |
MECHANICAL PROPERTIES ACCORDING TO UNSJ463 (AS PER TEMPER HO2)
| Range(mm) | From | To | UTS Min(MPa) | UTS Max(MPa) | PS Min(MPa) | Elongation Min(%) | Hardness Min(MPa) | Hardness Max(MPa) |
| Round(Dia) | 0.059 | 2.953 | 56 | 66 |
|
| 60 | 76 |
| Hex(A/F) | 0.118 | 2.756 | 56 | 66 | 一 |
| 60 | 76 |
| Square(A/F) | 0.118 | 2.362 | 56 | 66 |
|
| 60 | 76 |
| Range(mm) | From | To | UTS Min(MPa) | UTS Max(MPa) | PS Min(MPa) | Elongation Min(%) | Hardness Min(MPa) | Hardness Max(MPa) |
| Round(Dia) | 1.5 | 75 | 385 | 455 |
|
| 60 | 76 |
| Hex(A/F) | 3 | 70 | 385 | 455 | 一 |
| 60 | 76 |
| Square(A/F) | 3 | 60 | 385 | 455 |
|
| 60 | 76 |
| PHYSICAL PROPERTIES |
| Melting Point -Liquidus°F | 1680 |
| Density lb/cu in.at 68°F | 0.305 |
| Specific Gravity | 8.44 |
| Electrical Conductivity %IACS at 68°F | 27.6 |
| Thermal Conductivity Btu/ sq ft/ft hr/°F at 68°F | 67 |
| Coefficient of Thermal Expansion 68-57210-6 per°F(68-572° | 11.4 |
| Specific Heat Capacity Btu/lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tension ksi | 15000 |
| Modulus of Rigidity ksi | 5600 |
| FABRICATION PROPERTIES |
| No fabrication properties for this alloy |